Li-doped lead zirconate titanate film

Based on

1 Articles
2014 Most recent source

Composition

Image only illustrates the order and placement of components as described in literature.

1

Li-doped lead zirconate titanate

lead zirconium titanate Li-doped PZT
Type Complex Compound
Formula
Role layer
2

platinum

Type Single Compound
Formula Pt
Role layer

Properties

General physical and chemical properties

Property Value Nanomaterial Variant Source
coercive field

More information/entries available to subscribers only.

Or, view sample content

Applications

Area Application Nanomaterial Variant Source
electronics

More information available to subscribers only.

Or, view sample content

Characterization

Method Nanomaterial Variant Source
field emission scanning electron microscopy

More information/entries available to subscribers only.

Or, view sample content

Biological effects

Preparation

Method 1

Type: Physical formation
Source:
Starting materials
  • Pt-coated silicon
  • platinum
  • Li-doped lead zirconate titanate
Product

Li-doped lead zirconate titanate film

Diameter: ~ 400000 nm

Grain size: ~ 135 nm

Roughness: <= 1.5 nm

Thickness: ~ 100 nm

Thickness: ~ 2000 nm

Medium: none

Support: Pt-coated silicon

Method 2

Type: Physical formation
Source:
Starting materials
  • Pt-coated silicon
  • platinum
  • Li-doped lead zirconate titanate
Product

Li-doped lead zirconate titanate film

Diameter: ~ 400000 nm

Grain size: ~ 135 nm

Roughness: <= 1.5 nm

Thickness: ~ 100 nm

Thickness: ~ 2000 nm

Medium: none

Support: Pt-coated silicon

Method 3

Type: Physical formation
Source:
Starting materials
  • Pt-coated silicon
  • platinum
  • Li-doped lead zirconate titanate
Product

Li-doped lead zirconate titanate film

Diameter: ~ 400000 nm

Grain size: ~ 135 nm

Roughness: <= 1.5 nm

Thickness: ~ 100 nm

Thickness: ~ 2000 nm

Medium: none

Support: Pt-coated silicon

References

Full content is available to subscribers only

To view content please choose from the following:

We use cookies to improve your experience with our site. More information

Sign up for a free trial